HUATEC TG-100G Electrolytic Coulometric Coating Thickness Gauge
General introduction
1. TG-100G is more focused on the automobile, motorcycle, and sanitary ware industries, because these industries will use the potential difference function. And neodymium iron boron industry, to solve the test problems of the underlying nickel. Automobiles such as: signs, car door locks, car handles, car interior parts, motorcycles such as mufflers, motorcycle, brackets, sanitary wares such as: mixing water valves, towel racks, neodymium Iron-boron: mainly nickel-copper-nickel electroplating.
2. The surface of Ndfeb products is microporous. In the process of electrodeposition, nickel deposition penetrates into the pores of the matrix, forming an invisible interface. Therefore, there is no potential mutation unique to the conventional interface, and the conventional thickness measuring instrument cannot correctly determine the measurement end point.
3. Using TG-100G electrolytic thickness measuring instrument, using the thickness and potential measurement method can effectively solve the problem of Ndfeb permanent magnet coating measurement.
4. Multi-layer nickel coating is measured by TG-100G electrolytic thickness meter, which can analyze the thickness and potential difference of each nickel layer by curve.
5. Can be changed to two kinds of probe, usually 2.4mm and 1.7mm
6. Data can be stored in the computer at any time
7. Test report can be printed by A4 paper
8. Meet standards ASTM B764,DIN EN ISO 16866, Standard Test Method for Simultaneous Thickness and Electrode Potential Determination of Individual Layers in Multilayer Nickel Deposit (STEP Test)
Measure the thickness of electroplating on extremely thin wire with a diameter of only 0.025mm
Technical specification
|
Plating type
|
Single metal paiting layer
|
Composite multiple plating layer
|
Alloy plating layer
|
Multi-layer nickel
|
|
Cr,Ni,Cu, Zn,Sn,Ag, Au,Cd,Co, Pb etc.
|
Cr/Ni/Cu etc.
|
NiP,ZnNi, SZn,SPb etc.
|
The thickness of each layer of multilayer nickel and the potential difference between nickel layers
|
|
Substrate
|
Metal
|
Non-metal
|
|
Steel,copper,copper alloys, die-cast zinc,aluminum etc
|
Plastic,neodymium iron boron,ceramics etc
|
|
Measuring range
|
0.03～300μm
|
|
The best use range 0.03～50um,Over 50um,the error will gradually become larger
|
|
Resolution
|
0.01um
|
|
Repeatability
|
≤5%
|
|
Indication error
|
≤10%
|
|
Potential range
|
0～3000mv
|
|
Potential accuracy
|
0.01mv
|
|
Probe size
|
Standard:φ2.4,φ1.7(unit:mm)
Optional:φ1.2,φ1.0,φ0.8(unit:mm)
|
|
Wire test
|
Diameter 0.050～4mm
multi-layer coating thickness on the cylindrical surface, without conversion, direct reading
|
|
Test stand
|
Standard:STD07
Optional:STD16,STD19,STD-W wire test stand
|
|
Calibration
|
Factory calibration
calibrate a single coating with calibration foils or uniformly calibrate
|
|
Stop measurement
|
Automatic judgment
|
|
Stand-alone use
|
When not measuring the potential difference
|
|
Print
|
A laser or inkjet printer can be purchased separately to print A4 format test results, Excel format, content can be customized
In stand-alone use, a thermal printer can be used to print the test results
|
|
Print Content
|
Plating type, single measurement value, average value, maximum value, minimum value, standard deviation, coefficient of variation, time
Thickness-potential curve
|
|
Display mode
|
Online use:PC Screen display
Stand-alone use:126*64 dot LCD screen
|
|
Data stroage
|
PC Database
|
|
Test Hot Key
|
Stand-aone use,you can customize the hot key for single plating or multiple plating/substrate combination
|
|
Curve Analysis
|
can be displayed on the same screen and modified at will
|
|
Pause test
|
For thick coatings, you can pause at any time and continue the test after changing the electrolyte
|
|
Data check
|
multiple query methods
|
|
Operating system
|
win7,win10
|
|
Software upgrade
|
New products in December 2019, continuous upgrade
|
|
Power Supply
|
AC 220V, AC 110V can be customized
|
|
Host Size
|
200*255*161(mm)
|